{"id":11783,"date":"2026-06-19T12:10:12","date_gmt":"2026-06-19T04:10:12","guid":{"rendered":"https:\/\/www.cncmachiningshops.com\/?p=11783"},"modified":"2026-07-15T22:07:01","modified_gmt":"2026-07-15T14:07:01","slug":"metal-plating-process","status":"publish","type":"post","link":"https:\/\/www.cncmachiningshops.com\/tr\/metal-plating-process\/","title":{"rendered":"Metal Kaplama \u0130\u015flemi Se\u00e7imi: Do\u011fru Kaplama Nas\u0131l Se\u00e7ilir?"},"content":{"rendered":"
\n

Quick Answer:<\/strong> Metal plating is selected based on five application requirements \u2014 not by coating name. The five factors are: base material (adhesion and pre-treatment requirements vary by substrate), corrosion environment (salt spray resistance ranges from ~72\u2013240 hours for zinc to 500+ hours for nickel-chrome), wear conditions (hardness ranges from 50\u2013150 HV for zinc to 800\u20131,000 HV for hard chrome), electrical performance (silver provides the lowest contact resistance; gold provides stable low-resistance contacts over time), and dimensional tolerance (electroless nickel deposits uniformly to \u00b12\u20133 \u00b5m; electroplating builds thicker at edges). The coating is the output of these five decisions \u2014 not the starting point. Common failure modes are predictable: choosing zinc plating for marine environments produces corrosion within weeks; specifying electroplated nickel on a bore held to \u00b10.010 mm produces assembly interference because 10 \u00b5m per side equals 20 \u00b5m reduction in bore diameter; using nickel on electrical connectors causes rising contact resistance as the nickel oxide layer builds over time.<\/p><\/blockquote>\n

\n

The Five Factors That Determine the Correct Plating Process<\/h2>\n

Base Material<\/h3>\n

Every plating process requires that the coating bonds to the substrate through a stable metallurgical or chemical adhesion mechanism. Adhesion failure at this interface is the root cause of delamination and peeling \u2014 and it occurs before corrosion or wear ever become relevant.<\/p>\n

Steel and carbon steel bond reliably to zinc, nickel, chrome, and most standard platings after mechanical or chemical cleaning and acid activation. 1045 carbon steel, 4140 alloy steel, and mild steel are the most plating-compatible base materials; the process is relatively forgiving.<\/p>\n

Stainless steel has a passive oxide layer that must be chemically stripped (activated) immediately before plating. If the activation step is omitted or insufficient, the plating contacts the passive oxide film rather than the base metal \u2014 producing an adhesion joint that fails under thermal cycling, vibration, or mechanical stress.<\/p>\n

Aluminum requires a two-step pre-treatment: immersion in a zincate solution, which deposits a thin zinc layer directly on the aluminum surface, followed by the intended plating over the zinc interlayer. Without zincate pre-treatment, aluminum’s native oxide layer prevents bonding. An aluminum 6061 housing plated directly with electroless nickel without zincate will peel within weeks of thermal cycling (80\u2013120\u00b0C is sufficient to fail the interface). With proper zincate pre-treatment, the electroless nickel-on-zinc-on-aluminum system is stable and widely used in aerospace and electronics.<\/p>\n

Copper and copper alloys have high surface energy and accept most platings without special pre-treatment. They are commonly used as an intermediate underlayer (copper strike) to improve adhesion between difficult substrates and subsequent platings.<\/p>\n

Corrosion Environment<\/h3>\n

The corrosion performance requirement is environment-specific. Salt spray test results (ASTM B117) provide a relative comparison:<\/p>\n\n\n\n\n\n\n\n\n\n\n
Coating<\/th>\nTypical Salt Spray Resistance (with standard post-treatment)<\/th>\n<\/tr>\n<\/thead>\n
Zinc (chromate passivated)<\/td>\n72\u2013240 hours<\/td>\n<\/tr>\n
Zinc-nickel<\/td>\n500\u20131,000 hours<\/td>\n<\/tr>\n
Nickel<\/td>\n200\u2013500 hours<\/td>\n<\/tr>\n
Electroless nickel (high phosphorus)<\/td>\n500\u20131,000 hours<\/td>\n<\/tr>\n
Nickel + chrome<\/td>\n500+ hours<\/td>\n<\/tr>\n
Cadmium<\/td>\n500\u20131,000 hours<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

These numbers reflect relative performance under accelerated testing conditions \u2014 they do not directly translate to years of service, which depends on actual exposure intensity. For outdoor structural steel exposed to moderate humidity, 8\u201312 \u00b5m zinc with chromate passivation typically provides 1\u20132 years of service before visible corrosion. Marine environments (continuous salt spray, salt fog, or immersion) eliminate zinc-only coatings as an appropriate specification; nickel, electroless nickel, or zinc-nickel systems are required.<\/p>\n

Wear Conditions<\/h3>\n

Coating hardness is the primary predictor of wear performance under sliding or abrasive contact:<\/p>\n\n\n\n\n\n\n\n\n\n\n
Coating<\/th>\nApproximate Hardness<\/th>\n<\/tr>\n<\/thead>\n
Zinc<\/td>\n50\u2013150 HV<\/td>\n<\/tr>\n
Copper<\/td>\n60\u2013100 HV<\/td>\n<\/tr>\n
Nickel (electroplated)<\/td>\n200\u2013500 HV<\/td>\n<\/tr>\n
Electroless nickel (as-deposited)<\/td>\n450\u2013600 HV<\/td>\n<\/tr>\n
Electroless nickel (heat treated at 400\u00b0C)<\/td>\n900\u20131,100 HV<\/td>\n<\/tr>\n
Hard chrome<\/td>\n800\u20131,000 HV<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

A steel shaft plated with zinc operating in a linear motion guide (5,000\u201310,000 cycles) will show coating wear and substrate exposure within thousands of cycles \u2014 the 50\u2013150 HV zinc layer cannot resist the contact stresses of repeated sliding. The same shaft with 20\u201330 \u00b5m hard chrome at 800\u20131,000 HV maintains dimensional integrity and surface finish across hundreds of thousands of cycles. Hard chrome on hydraulic piston rods is an industry standard for this reason \u2014 the hydraulic rod requires consistent surface hardness, precise diameter, and low surface roughness (Ra \u2264 0.4 \u00b5m) maintained over the full operating life.<\/p>\n

Electrical Performance<\/h3>\n

Conductivity, contact resistance, and oxidation stability determine plating selection for electrical components:<\/p>\n

    \n
  • Silver<\/strong> has the lowest bulk resistivity of all metals (~1.6 \u00b5\u03a9\u00b7cm) and produces the lowest initial contact resistance. It is the correct choice for high-current connectors and RF contacts where every fraction of milliohm matters. Silver tarnishes (silver sulfide formation) in air containing sulfur compounds, which increases contact resistance in signal applications.<\/li>\n
  • Gold<\/strong> does not oxidize under any service condition and maintains stable contact resistance below 1 m\u03a9 over the full service life. Gold plating of 0.5\u20133 \u00b5m on a nickel underlayer is the standard for low-voltage signal connectors in aerospace, medical, and precision electronics. Gold is not appropriate as a wear coating \u2014 its hardness is approximately 100\u2013200 HV, and it wears rapidly under repeated mechanical contact. Gold is specified for electrical contacts, not structural surfaces.<\/li>\n
  • Tin<\/strong> is solderable, resists oxidation better than bare copper, and is the standard plating for through-hole and surface-mount connector leads. Tin whisker growth (spontaneous tin filament growth under compression) is a known risk in pure tin plating, mitigated by using tin-lead alloys (restricted under RoHS) or matte tin with controlled grain structure.<\/li>\n
  • Nickel<\/strong> provides moderate conductivity but forms a resistive oxide layer on the surface over time, particularly in environments with intermittent current or in low-force contact applications. Nickel-only connectors that perform acceptably at installation often develop rising contact resistance after months of service as the oxide layer grows.<\/li>\n<\/ul>\n

    Manufacturing Cost<\/h3>\n

    Cost follows a non-linear progression that reflects both process complexity and material value:<\/p>\n\n\n\n\n\n\n\n\n\n\n
    Coating<\/th>\nApproximate Relative Cost<\/th>\n<\/tr>\n<\/thead>\n
    Zinc<\/td>\n1\u00d7 (baseline)<\/td>\n<\/tr>\n
    Nickel (electroplated)<\/td>\n1.5\u20132\u00d7<\/td>\n<\/tr>\n
    Electroless nickel<\/td>\n2\u20134\u00d7<\/td>\n<\/tr>\n
    Hard chrome<\/td>\n3\u20135\u00d7<\/td>\n<\/tr>\n
    Silver<\/td>\n5\u201310\u00d7<\/td>\n<\/tr>\n
    Gold (full surface)<\/td>\n10\u201350\u00d7+<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n

    These ratios apply to processing cost per part at typical thicknesses and production volumes. Selective plating \u2014 applying gold only to the electrical contact area of a connector while using nickel on the housing \u2014 is standard practice for cost control and is technically straightforward with masking.<\/p>\n

    \n

    Plating Process Comparison<\/h2>\n\n\n\n\n\n\n\n\n\n\n\n\n
    Process<\/th>\nCorrosion Resistance<\/th>\nHardness<\/th>\nElectrical<\/th>\nThickness Control<\/th>\nTypical Applications<\/th>\n<\/tr>\n<\/thead>\n
    Zinc<\/td>\nMedium<\/td>\n50\u2013150 HV<\/td>\nPoor<\/td>\nModerate<\/td>\nFasteners, brackets, general steel<\/td>\n<\/tr>\n
    Nickel (electroplated)<\/td>\nMedium\u2013high<\/td>\n200\u2013500 HV<\/td>\nModerate<\/td>\nModerate (edge buildup)<\/td>\nShafts, housings, decorative\/functional<\/td>\n<\/tr>\n
    Electroless nickel<\/td>\nHigh<\/td>\n450\u2013600 HV (900+ HV heat treated)<\/td>\nModerate<\/td>\nExcellent (\u00b12\u20133 \u00b5m)<\/td>\nPrecision parts, valves, complex geometry<\/td>\n<\/tr>\n
    Hard chrome<\/td>\nHigh<\/td>\n800\u20131,000 HV<\/td>\nLow\u2013moderate<\/td>\nRequires grinding<\/td>\nHydraulic rods, molds, wear surfaces<\/td>\n<\/tr>\n
    Copper<\/td>\nLow<\/td>\n60\u2013100 HV<\/td>\nExcellent<\/td>\nModerate<\/td>\nUnderlayer, EMI shielding, thermal conductors<\/td>\n<\/tr>\n
    Tin<\/td>\nMedium<\/td>\n20\u201340 HV<\/td>\nGood<\/td>\nModerate<\/td>\nConnector leads, solderable surfaces<\/td>\n<\/tr>\n
    Silver<\/td>\nMedium<\/td>\n60\u2013120 HV<\/td>\nExcellent (lowest resistance)<\/td>\nGood<\/td>\nRF connectors, high-current contacts<\/td>\n<\/tr>\n
    Gold<\/td>\nHigh (non-oxidizing)<\/td>\n100\u2013200 HV<\/td>\nExcellent (most stable)<\/td>\nGood (0.5\u20133 \u00b5m typical)<\/td>\nSignal connectors, aerospace electronics<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n
    \n

    How Plating Affects Tolerances and Dimensions<\/h2>\n

    Plating adds material to all exposed surfaces of the part. This dimensional addition is not optional and cannot be ignored for any component where dimensional fit is functional.<\/p>\n

    The basic calculation:<\/strong> An electroplated or electroless nickel coating of 10 \u00b5m on a shaft increases the shaft diameter by 20 \u00b5m (0.020 mm) \u2014 because the coating builds on all sides. The same 10 \u00b5m coating deposited inside a bore decreases the bore diameter by 20 \u00b5m. For a bore machined to \u00d820.000 mm with a tolerance of \u00b10.010 mm (acceptance range 19.990\u201320.010 mm), a 10 \u00b5m electroless nickel coating produces a final bore of approximately 19.980 mm \u2014 10 \u00b5m below the minimum acceptable dimension, meaning the part fails.<\/p>\n

    Thread interference:<\/strong> Threads are particularly sensitive to plating buildup. Zinc plating at 10 \u00b5m on an M8 bolt increases the thread flanks and major diameter. If the mating nut is also zinc plated, the combined dimensional interference on both thread components can make assembly impossible or produce galling during assembly. Standard practice is either to plate only one component (bolt or nut), to oversize the thread before plating, or to chase the thread after plating.<\/p>\n

    Uniformity difference between processes:<\/strong><\/p>\n

      \n
    • Electroplating (zinc, nickel): Deposit thickness follows the current density distribution on the part surface. Edges, corners, and projections receive higher current density and build up more coating (edge effect). Recesses, deep holes, and blind features receive less coating. Thickness variation of 3\u20135:1 (edge to recess) is typical.<\/li>\n
    • Electroless nickel: Deposition is chemically driven, not current-driven. The reaction rate is uniform across the entire part surface regardless of geometry. Thickness variation of \u00b110\u201315% of nominal (\u00b12\u20133 \u00b5m on a 15 \u00b5m deposit) is achieved even in blind holes, undercuts, and complex geometry. This predictability makes electroless nickel the preferred plating for tight-tolerance components.<\/li>\n<\/ul>\n

      Design for manufacture recommendations:<\/strong><\/p>\n

        \n
      • For shafts that will be plated, machine the shaft undersize by the plating allowance: if the target final diameter is 20.000 mm and the plating will be 10 \u00b5m, machine to 19.980 mm.<\/li>\n
      • For bores that will be internally plated, machine oversize by the plating allowance.<\/li>\n
      • For threads, specify whether threading occurs before or after plating \u2014 and if before plating, whether the mating component will also be plated.<\/li>\n
      • For the tightest tolerances (\u00b10.005\u20130.010 mm), specify the plating thickness as a range (“Electroless nickel, 8\u201312 \u00b5m”) and verify with post-plating measurement before assembly.<\/li>\n<\/ul>\n
        \n

        Common Plating Failures and How to Prevent Them<\/h2>\n

        Peeling and delamination:<\/strong> Adhesion failure between coating and substrate \u2014 the most visible failure mode. Caused by inadequate surface preparation (residual oil, oxide, or machining fluid on the substrate), incorrect activation sequence for difficult substrates (aluminum without zincate, stainless without activation), or incompatible base-coating metallurgy. Prevention: specify the pre-treatment sequence on the drawing or in the purchase specification \u2014 not just the coating type. For aluminum, state “zincate pre-treatment required.” For stainless, state “activation required.”<\/p>\n

        Hydrogen embrittlement in high-strength steel:<\/strong> During electroplating (particularly acid processes), hydrogen ions are generated at the cathode and absorbed into the steel substrate. In high-strength steel (above approximately 1,000 MPa tensile strength, equivalent to approximately grade 10.9 fasteners and above), the absorbed hydrogen produces internal stress cracking \u2014 delayed brittle fracture that can occur hours or days after plating, under load levels well below the yield strength. Prevention: baking at 180\u2013220\u00b0C for 8\u201324 hours after plating (per ASTM B242 or similar specification) drives out the absorbed hydrogen. For safety-critical fasteners above this strength threshold, hydrogen embrittlement risk must be explicitly addressed in the process specification.<\/p>\n

        Corrosion beneath the coating:<\/strong> Corrosion beginning under the plating surface, invisible until the coating blisters or lifts. Caused by coating porosity (thin deposits have more through-pores), geometric coverage gaps (electroplating leaving thin or uncoated zones in recesses), or moisture ingress through edge gaps. Prevention: specify minimum coating thickness appropriate for the environment (not minimum acceptable \u2014 minimum that provides reliable barrier protection); use electroless nickel for complex geometry where coverage uniformity is critical.<\/p>\n

        Rising contact resistance in electrical connectors:<\/strong> Nickel oxide formation on connector contact surfaces increases contact resistance from initial acceptable values to functional failure levels over months of service in low-force contact applications. Prevention: use gold flash (0.5\u20131.5 \u00b5m) over nickel underlayer for all signal contact surfaces; do not rely on nickel alone for low-voltage contacts.<\/p>\n

        \n

        Application Guide<\/h2>\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n\n
        Application<\/th>\nRecommended Coating<\/th>\nPrimary Reason<\/th>\n<\/tr>\n<\/thead>\n
        Outdoor steel fasteners (general)<\/td>\nZinc, 8\u201312 \u00b5m, chromate passivated<\/td>\nCost-effective sacrificial protection<\/td>\n<\/tr>\n
        Outdoor fasteners, coastal\/marine<\/td>\nZinc-nickel or nickel<\/td>\nZinc alone insufficient for salt environment<\/td>\n<\/tr>\n
        High-strength fasteners (>1,000 MPa)<\/td>\nZinc with mandatory post-bake, or mechanical coating<\/td>\nHydrogen embrittlement risk requires baking or non-acid process<\/td>\n<\/tr>\n
        Hydraulic cylinder rods<\/td>\nHard chrome, post-ground to Ra \u22640.4 \u00b5m<\/td>\nWear resistance, dimensional precision, oil-film retention<\/td>\n<\/tr>\n
        Precision valve spools and bores<\/td>\nElectroless nickel, 8\u201315 \u00b5m<\/td>\nUniform coating; tight tolerance retention<\/td>\n<\/tr>\n
        Automotive exterior components<\/td>\nZinc-nickel or nickel-chrome<\/td>\nCorrosion resistance + cycle life in road salt<\/td>\n<\/tr>\n
        Signal connectors (low voltage)<\/td>\nGold, 1\u20133 \u00b5m over nickel underlayer<\/td>\nStable contact resistance; non-oxidizing<\/td>\n<\/tr>\n
        High-current power connectors<\/td>\nSilver, 5\u201315 \u00b5m<\/td>\nLowest contact resistance; highest conductivity<\/td>\n<\/tr>\n
        Solderable connector leads<\/td>\nMatte tin<\/td>\nSolderability; whisker risk controlled by grain structure<\/td>\n<\/tr>\n
        Aerospace structural fasteners<\/td>\nElectroless nickel or cadmium (where approved)<\/td>\nReliability, dimensional predictability, corrosion performance<\/td>\n<\/tr>\n
        Aluminum housing (electronics)<\/td>\nZincate + electroless nickel<\/td>\nUniform coverage; adhesion on aluminum<\/td>\n<\/tr>\n
        Industrial gear shafts<\/td>\nNickel or phosphate + oil<\/td>\nBalanced wear and corrosion; lubrication compatibility<\/td>\n<\/tr>\n
        Medical instrument components<\/td>\nElectroless nickel (or passivated stainless)<\/td>\nSurface smoothness; cleanability; chemical resistance<\/td>\n<\/tr>\n<\/tbody>\n<\/table>\n
        \n

        Key Takeaways<\/h2>\n
          \n
        • The plating process is determined by five application requirements \u2014 base material, corrosion environment, wear conditions, electrical performance, and dimensional tolerance \u2014 not by preference or convention<\/strong>: selecting the coating first and checking the requirements second is the primary cause of plating failures in manufactured products.<\/li>\n
        • Electroless nickel is the correct plating for tight-tolerance components<\/strong>: its chemically driven deposition produces \u00b12\u20133 \u00b5m thickness uniformity even in blind holes, undercuts, and complex geometry, where electroplating produces 3\u20135\u00d7 edge buildup relative to recesses.<\/li>\n
        • Plating adds 2\u00d7 the layer thickness to every diametered feature<\/strong>: a 10 \u00b5m coating adds 0.020 mm to a shaft diameter and subtracts 0.020 mm from a bore diameter. For any tolerance tighter than \u00b10.050 mm, the plating allowance must be incorporated in the pre-plating machining dimension.<\/li>\n
        • Hard chrome at 800\u20131,000 HV is the correct coating for severe sliding wear applications<\/strong>: hydraulic rods, mold wear surfaces, and high-cycle linear motion components. No standard plating option approaches this hardness; electroless nickel heat treated to 900\u20131,100 HV is an alternative when chromium’s environmental and dimensional post-processing considerations are limiting.<\/li>\n
        • Gold is specified for stable electrical contact resistance, not for corrosion protection or wear resistance<\/strong>: 0.5\u20133 \u00b5m gold over a nickel underlayer provides a non-oxidizing, dimensionally stable contact surface with contact resistance below 1 m\u03a9 that does not degrade over service life. Gold should not be used where wear is the failure mode \u2014 its 100\u2013200 HV hardness is among the lowest of all plating options.<\/li>\n
        • Hydrogen embrittlement is a silent failure mode for high-strength steel above approximately 1,000 MPa<\/strong>: electroplating processes generate hydrogen that absorbs into the steel substrate and produces delayed brittle fracture under load. Post-plating baking (ASTM B242 or equivalent) is mandatory for grade 10.9 and 12.9 fasteners and other high-strength steel components.<\/li>\n
        • For OEM procurement and design teams<\/strong>: plating specifications on engineering drawings should include coating type, thickness range with tolerance (e.g., “Electroless nickel per ASTM B733, Class 1, 10 \u00b5m \u00b12 \u00b5m”), pre-treatment requirements for non-ferrous substrates (e.g., “Zincate pre-treatment required for aluminum substrate”), and any post-plating requirements (e.g., “Post-plate baking per ASTM B242, 200\u00b0C, 8 hours, required for base material UTS >1,000 MPa”). Drawing notes that specify only “nickel plated” without thickness, tolerance, and substrate-specific requirements leave process decisions to the supplier and create risk of receiving parts that fail function or dimensional requirements.<\/li>\n<\/ul>\n
          \n

          Frequently Asked Questions<\/h2>\n

          How do I choose the right metal plating process?<\/h3>\n

          The correct approach is to define five requirements before evaluating any coating: base material (determines adhesion and pre-treatment requirements), corrosion environment (determines minimum protective performance), wear conditions (determines minimum hardness), electrical requirements (determines conductivity and oxidation stability needs), and dimensional tolerance (determines whether uniform or electroplated deposition is required). Once these five are defined, the coating options that meet all five requirements are identified \u2014 typically one or two processes \u2014 and cost determines the final selection. Starting with a coating name and checking whether it fits the requirements afterward produces significantly more mismatches than starting with requirements.<\/p>\n

          What is the difference between electroless nickel and electroplated nickel?<\/h3>\n

          Electroplated nickel uses electrical current to drive nickel ions onto the substrate. The deposition rate follows current density distribution \u2014 edges and projections receive more coating, recesses and holes receive less, producing thickness variation of approximately 3\u20135:1 across complex geometry. Electroless nickel uses a chemical reduction reaction that does not require current. The deposition rate is uniform across all accessible surfaces regardless of geometry, producing thickness variation of \u00b110\u201315% of nominal (\u00b12\u20133 \u00b5m on a typical 15 \u00b5m deposit) even inside blind holes and undercuts. For tight-tolerance components (\u00b10.010\u20130.025 mm), electroless nickel’s dimensional predictability makes it the required choice. Electroplated nickel is appropriate for less critical geometry where cost is more important than uniformity.<\/p>\n

          How does plating thickness affect part tolerances?<\/h3>\n

          Plating deposits on all exposed surfaces. The dimensional effect is straightforward: plating thickness T adds 2T to the diameter of any external cylindrical feature (shaft, pin) and subtracts 2T from the diameter of any internal cylindrical feature (bore, hole). Flat surfaces increase in thickness by T per surface. For a shaft at nominal 20.000 mm plated with 10 \u00b5m nickel, the final diameter is approximately 20.020 mm. If the tolerance is \u00b10.010 mm (acceptable range 19.990\u201320.010 mm), the plated shaft at 20.020 mm is outside tolerance. Correct practice is to machine the shaft undersize by the plating allowance before plating, or to specify post-plating grinding to final dimension.<\/p>\n

          When is gold plating required versus other conductive coatings?<\/h3>\n

          Gold plating is required when stable contact resistance over the full service life is the primary requirement \u2014 specifically in low-voltage signal applications (below approximately 5V), where even a small increase in contact resistance produces measurable signal degradation, and in applications that must perform reliably after years of service without maintenance access. Gold does not oxidize under any service condition, maintaining contact resistance below 1 m\u03a9 throughout its service life. Silver is preferred for high-current applications (above approximately 5A) where the lowest initial resistance is critical and some tarnishing is acceptable. Tin is used where solderability is required and contact resistance can tolerate the thin tin oxide layer that forms over time.<\/p>\n

          What causes hydrogen embrittlement in plated steel fasteners?<\/h3>\n

          Hydrogen embrittlement occurs during electroplating when hydrogen ions (generated at the part surface during acid cleaning and electrodeposition) absorb into the steel lattice. In high-strength steel (above approximately 1,000 MPa tensile strength), absorbed hydrogen produces microcracks at stress concentrations, causing delayed brittle fracture under normal service loads \u2014 sometimes hours or days after plating completion. The failure is sudden and occurs without the plastic deformation or visible warning that characterizes ductile overload failure. Prevention requires baking the plated parts immediately after plating (within 4 hours) at 180\u2013220\u00b0C for 8\u201324 hours per ASTM B242, which drives the absorbed hydrogen out of the steel. This baking requirement applies to all grade 10.9 and 12.9 fasteners and to any high-strength steel component where hydrogen embrittlement failure would be safety-critical.<\/p>\n

          \n

          Written by the CMS engineering team with 15+ years of precision CNC machining experience specifying and coordinating surface treatment processes \u2014 including electroless nickel, hard chrome, zinc, gold, and silver plating \u2014 for automotive, aerospace, medical device, electronics, and industrial OEM manufacturing programs. Technical references: ASTM B117 (Salt Spray Testing), ASTM B242 (Hydrogen Embrittlement Relief Baking), ASTM B733 (Electroless Nickel per Coating Class), ASTM B456 (Nickel-Chrome Electrodeposit), ASM Handbook Vol. 5 (Surface Engineering \u2014 Electroplating chapters), Snyder D.L. \u2014 Electroplating Engineering Handbook.<\/em><\/p>\n

          \n

          Sourcing CNC Machined Components Requiring Surface Plating?<\/strong><\/p>\n

          At CMS, we coordinate surface treatment specifications for CNC machined components \u2014 including electroless nickel, hard chrome, zinc, gold flash, and specialty coatings \u2014 with dimensional verification before and after plating to confirm tolerance compliance.<\/p>\n

          [Request a surface treatment specification review and CNC machining quote \u2192]<\/p>\n<\/div>\n","protected":false},"excerpt":{"rendered":"

          Metal plating process: zinc, nickel, electroless nickel, hard chrome, gold & silver \u2014 selection by corrosion, wear, conductivity, tolerance & cost guide.<\/p>","protected":false},"author":1,"featured_media":11853,"comment_status":"open","ping_status":"open","sticky":false,"template":"","format":"standard","meta":{"footnotes":""},"categories":[165],"tags":[],"class_list":["post-11783","post","type-post","status-publish","format-standard","has-post-thumbnail","hentry","category-surface-treatment-guide"],"yoast_head":"\nMetal Plating Process Selection: How to Choose the Right Coating<\/title>\n<meta name=\"description\" content=\"Metal plating process: zinc, nickel, electroless nickel, hard chrome, gold & silver \u2014 selection by corrosion, wear, conductivity, tolerance & cost guide.\" \/>\n<meta name=\"robots\" content=\"index, follow, max-snippet:-1, max-image-preview:large, max-video-preview:-1\" \/>\n<link rel=\"canonical\" href=\"https:\/\/www.cncmachiningshops.com\/tr\/metal-plating-process\/\" \/>\n<meta property=\"og:locale\" content=\"tr_TR\" \/>\n<meta property=\"og:type\" content=\"article\" \/>\n<meta property=\"og:title\" content=\"Metal Plating Process Selection: How to Choose the Right Coating\" \/>\n<meta property=\"og:description\" content=\"Metal plating process: zinc, nickel, electroless nickel, hard chrome, gold & silver \u2014 selection by corrosion, wear, conductivity, tolerance & cost guide.\" \/>\n<meta property=\"og:url\" content=\"https:\/\/www.cncmachiningshops.com\/tr\/metal-plating-process\/\" \/>\n<meta property=\"og:site_name\" content=\"CNC Machining Shops\" \/>\n<meta property=\"article:published_time\" content=\"2026-06-19T04:10:12+00:00\" \/>\n<meta property=\"article:modified_time\" content=\"2026-07-15T14:07:01+00:00\" \/>\n<meta name=\"author\" content=\"cncmachiningshops\" \/>\n<meta name=\"twitter:card\" content=\"summary_large_image\" \/>\n<meta name=\"twitter:label1\" content=\"Yazan:\" \/>\n\t<meta name=\"twitter:data1\" content=\"cncmachiningshops\" \/>\n\t<meta name=\"twitter:label2\" content=\"Tahmini okuma s\u00fcresi\" \/>\n\t<meta name=\"twitter:data2\" content=\"14 dakika\" \/>\n<script type=\"application\/ld+json\" class=\"yoast-schema-graph\">{\"@context\":\"https:\\\/\\\/schema.org\",\"@graph\":[{\"@type\":\"Article\",\"@id\":\"https:\\\/\\\/www.cncmachiningshops.com\\\/metal-plating-process\\\/#article\",\"isPartOf\":{\"@id\":\"https:\\\/\\\/www.cncmachiningshops.com\\\/metal-plating-process\\\/\"},\"author\":{\"name\":\"cncmachiningshops\",\"@id\":\"https:\\\/\\\/www.cncmachiningshops.com\\\/#\\\/schema\\\/person\\\/2593a2e2de68be71300e10f486236551\"},\"headline\":\"Metal Plating Process Selection: How to Choose the Right Coating\",\"datePublished\":\"2026-06-19T04:10:12+00:00\",\"dateModified\":\"2026-07-15T14:07:01+00:00\",\"mainEntityOfPage\":{\"@id\":\"https:\\\/\\\/www.cncmachiningshops.com\\\/metal-plating-process\\\/\"},\"wordCount\":3025,\"commentCount\":0,\"publisher\":{\"@id\":\"https:\\\/\\\/www.cncmachiningshops.com\\\/#organization\"},\"image\":{\"@id\":\"https:\\\/\\\/www.cncmachiningshops.com\\\/metal-plating-process\\\/#primaryimage\"},\"thumbnailUrl\":\"https:\\\/\\\/www.cncmachiningshops.com\\\/wp-content\\\/uploads\\\/2026\\\/06\\\/Metal-Plating-Process-Selection-800x600-1.jpg\",\"articleSection\":[\"Surface Treatment Guide\"],\"inLanguage\":\"tr\",\"potentialAction\":[{\"@type\":\"CommentAction\",\"name\":\"Comment\",\"target\":[\"https:\\\/\\\/www.cncmachiningshops.com\\\/metal-plating-process\\\/#respond\"]}]},{\"@type\":\"WebPage\",\"@id\":\"https:\\\/\\\/www.cncmachiningshops.com\\\/metal-plating-process\\\/\",\"url\":\"https:\\\/\\\/www.cncmachiningshops.com\\\/metal-plating-process\\\/\",\"name\":\"Metal Plating Process Selection: How to Choose the Right Coating\",\"isPartOf\":{\"@id\":\"https:\\\/\\\/www.cncmachiningshops.com\\\/#website\"},\"primaryImageOfPage\":{\"@id\":\"https:\\\/\\\/www.cncmachiningshops.com\\\/metal-plating-process\\\/#primaryimage\"},\"image\":{\"@id\":\"https:\\\/\\\/www.cncmachiningshops.com\\\/metal-plating-process\\\/#primaryimage\"},\"thumbnailUrl\":\"https:\\\/\\\/www.cncmachiningshops.com\\\/wp-content\\\/uploads\\\/2026\\\/06\\\/Metal-Plating-Process-Selection-800x600-1.jpg\",\"datePublished\":\"2026-06-19T04:10:12+00:00\",\"dateModified\":\"2026-07-15T14:07:01+00:00\",\"description\":\"Metal plating process: zinc, nickel, electroless nickel, hard chrome, gold & silver \u2014 selection by corrosion, wear, conductivity, tolerance & cost guide.\",\"breadcrumb\":{\"@id\":\"https:\\\/\\\/www.cncmachiningshops.com\\\/metal-plating-process\\\/#breadcrumb\"},\"inLanguage\":\"tr\",\"potentialAction\":[{\"@type\":\"ReadAction\",\"target\":[\"https:\\\/\\\/www.cncmachiningshops.com\\\/metal-plating-process\\\/\"]}]},{\"@type\":\"ImageObject\",\"inLanguage\":\"tr\",\"@id\":\"https:\\\/\\\/www.cncmachiningshops.com\\\/metal-plating-process\\\/#primaryimage\",\"url\":\"https:\\\/\\\/www.cncmachiningshops.com\\\/wp-content\\\/uploads\\\/2026\\\/06\\\/Metal-Plating-Process-Selection-800x600-1.jpg\",\"contentUrl\":\"https:\\\/\\\/www.cncmachiningshops.com\\\/wp-content\\\/uploads\\\/2026\\\/06\\\/Metal-Plating-Process-Selection-800x600-1.jpg\",\"width\":800,\"height\":600,\"caption\":\"Metal Plating Process Selection 800x600\"},{\"@type\":\"BreadcrumbList\",\"@id\":\"https:\\\/\\\/www.cncmachiningshops.com\\\/metal-plating-process\\\/#breadcrumb\",\"itemListElement\":[{\"@type\":\"ListItem\",\"position\":1,\"name\":\"Home\",\"item\":\"https:\\\/\\\/www.cncmachiningshops.com\\\/\"},{\"@type\":\"ListItem\",\"position\":2,\"name\":\"Metal Plating Process Selection: How to Choose the Right Coating\"}]},{\"@type\":\"WebSite\",\"@id\":\"https:\\\/\\\/www.cncmachiningshops.com\\\/#website\",\"url\":\"https:\\\/\\\/www.cncmachiningshops.com\\\/\",\"name\":\"CNC Machining Shops\",\"description\":\"10+ Years CNC Machining Service Supplier\",\"publisher\":{\"@id\":\"https:\\\/\\\/www.cncmachiningshops.com\\\/#organization\"},\"alternateName\":\"CMS\",\"potentialAction\":[{\"@type\":\"SearchAction\",\"target\":{\"@type\":\"EntryPoint\",\"urlTemplate\":\"https:\\\/\\\/www.cncmachiningshops.com\\\/?s={search_term_string}\"},\"query-input\":{\"@type\":\"PropertyValueSpecification\",\"valueRequired\":true,\"valueName\":\"search_term_string\"}}],\"inLanguage\":\"tr\"},{\"@type\":\"Organization\",\"@id\":\"https:\\\/\\\/www.cncmachiningshops.com\\\/#organization\",\"name\":\"CNC Machining Shops\",\"alternateName\":\"CMS\",\"url\":\"https:\\\/\\\/www.cncmachiningshops.com\\\/\",\"logo\":{\"@type\":\"ImageObject\",\"inLanguage\":\"tr\",\"@id\":\"https:\\\/\\\/www.cncmachiningshops.com\\\/#\\\/schema\\\/logo\\\/image\\\/\",\"url\":\"https:\\\/\\\/www.cncmachiningshops.com\\\/wp-content\\\/uploads\\\/2025\\\/11\\\/CMS_Logo_1000x1000.png\",\"contentUrl\":\"https:\\\/\\\/www.cncmachiningshops.com\\\/wp-content\\\/uploads\\\/2025\\\/11\\\/CMS_Logo_1000x1000.png\",\"width\":800,\"height\":800,\"caption\":\"CNC Machining Shops\"},\"image\":{\"@id\":\"https:\\\/\\\/www.cncmachiningshops.com\\\/#\\\/schema\\\/logo\\\/image\\\/\"},\"description\":\"Shenzhen CMS Technology Co., Ltd. is located in Shenzhen, Guangdong, China. It was established in 2012 with a factory area of \u200b\u200b3,000 square meters. It is a company specializing in CNC machining and precision parts manufacturing. We have passed ISO9001, IATF16949, ISO13485 certification and are your trusted partner.\",\"email\":\"info@cncmachiningshops.com\",\"telephone\":\"+8617196430663\",\"legalName\":\"Shenzhen CMS Technology Co., Ltd.\",\"foundingDate\":\"2012-07-22\",\"numberOfEmployees\":{\"@type\":\"QuantitativeValue\",\"minValue\":\"11\",\"maxValue\":\"50\"}},{\"@type\":\"Person\",\"@id\":\"https:\\\/\\\/www.cncmachiningshops.com\\\/#\\\/schema\\\/person\\\/2593a2e2de68be71300e10f486236551\",\"name\":\"cncmachiningshops\",\"image\":{\"@type\":\"ImageObject\",\"inLanguage\":\"tr\",\"@id\":\"https:\\\/\\\/secure.gravatar.com\\\/avatar\\\/36a63d96ed08f8805561107422de4e83bbf8d1669dbc9655acab534bc3e1ed17?s=96&d=mm&r=g\",\"url\":\"https:\\\/\\\/secure.gravatar.com\\\/avatar\\\/36a63d96ed08f8805561107422de4e83bbf8d1669dbc9655acab534bc3e1ed17?s=96&d=mm&r=g\",\"contentUrl\":\"https:\\\/\\\/secure.gravatar.com\\\/avatar\\\/36a63d96ed08f8805561107422de4e83bbf8d1669dbc9655acab534bc3e1ed17?s=96&d=mm&r=g\",\"caption\":\"cncmachiningshops\"},\"sameAs\":[\"https:\\\/\\\/cncmachiningshops.com\"]}]}<\/script>\n<!-- \/ Yoast SEO Premium plugin. -->","yoast_head_json":{"title":"Metal Kaplama \u0130\u015flemi Se\u00e7imi: Do\u011fru Kaplama Nas\u0131l Se\u00e7ilir?","description":"Metal kaplama prosesi: \u00e7inko, nikel, elektriksiz nikel, sert krom, alt\u0131n ve g\u00fcm\u00fc\u015f \u2014 korozyon, a\u015f\u0131nma, iletkenlik, tolerans ve maliyete g\u00f6re se\u00e7im k\u0131lavuzu.","robots":{"index":"index","follow":"follow","max-snippet":"max-snippet:-1","max-image-preview":"max-image-preview:large","max-video-preview":"max-video-preview:-1"},"canonical":"https:\/\/www.cncmachiningshops.com\/tr\/metal-plating-process\/","og_locale":"tr_TR","og_type":"article","og_title":"Metal Plating Process Selection: How to Choose the Right Coating","og_description":"Metal plating process: zinc, nickel, electroless nickel, hard chrome, gold & silver \u2014 selection by corrosion, wear, conductivity, tolerance & cost guide.","og_url":"https:\/\/www.cncmachiningshops.com\/tr\/metal-plating-process\/","og_site_name":"CNC Machining Shops","article_published_time":"2026-06-19T04:10:12+00:00","article_modified_time":"2026-07-15T14:07:01+00:00","author":"cncmachiningshops","twitter_card":"summary_large_image","twitter_misc":{"Yazan:":"cncmachiningshops","Tahmini okuma s\u00fcresi":"14 dakika"},"schema":{"@context":"https:\/\/schema.org","@graph":[{"@type":"Article","@id":"https:\/\/www.cncmachiningshops.com\/metal-plating-process\/#article","isPartOf":{"@id":"https:\/\/www.cncmachiningshops.com\/metal-plating-process\/"},"author":{"name":"cncmachiningshops","@id":"https:\/\/www.cncmachiningshops.com\/#\/schema\/person\/2593a2e2de68be71300e10f486236551"},"headline":"Metal Plating Process Selection: How to Choose the Right Coating","datePublished":"2026-06-19T04:10:12+00:00","dateModified":"2026-07-15T14:07:01+00:00","mainEntityOfPage":{"@id":"https:\/\/www.cncmachiningshops.com\/metal-plating-process\/"},"wordCount":3025,"commentCount":0,"publisher":{"@id":"https:\/\/www.cncmachiningshops.com\/#organization"},"image":{"@id":"https:\/\/www.cncmachiningshops.com\/metal-plating-process\/#primaryimage"},"thumbnailUrl":"https:\/\/www.cncmachiningshops.com\/wp-content\/uploads\/2026\/06\/Metal-Plating-Process-Selection-800x600-1.jpg","articleSection":["Surface Treatment Guide"],"inLanguage":"tr","potentialAction":[{"@type":"CommentAction","name":"Comment","target":["https:\/\/www.cncmachiningshops.com\/metal-plating-process\/#respond"]}]},{"@type":"WebPage","@id":"https:\/\/www.cncmachiningshops.com\/metal-plating-process\/","url":"https:\/\/www.cncmachiningshops.com\/metal-plating-process\/","name":"Metal Kaplama \u0130\u015flemi Se\u00e7imi: Do\u011fru Kaplama Nas\u0131l Se\u00e7ilir?","isPartOf":{"@id":"https:\/\/www.cncmachiningshops.com\/#website"},"primaryImageOfPage":{"@id":"https:\/\/www.cncmachiningshops.com\/metal-plating-process\/#primaryimage"},"image":{"@id":"https:\/\/www.cncmachiningshops.com\/metal-plating-process\/#primaryimage"},"thumbnailUrl":"https:\/\/www.cncmachiningshops.com\/wp-content\/uploads\/2026\/06\/Metal-Plating-Process-Selection-800x600-1.jpg","datePublished":"2026-06-19T04:10:12+00:00","dateModified":"2026-07-15T14:07:01+00:00","description":"Metal kaplama prosesi: \u00e7inko, nikel, elektriksiz nikel, sert krom, alt\u0131n ve g\u00fcm\u00fc\u015f \u2014 korozyon, a\u015f\u0131nma, iletkenlik, tolerans ve maliyete g\u00f6re se\u00e7im k\u0131lavuzu.","breadcrumb":{"@id":"https:\/\/www.cncmachiningshops.com\/metal-plating-process\/#breadcrumb"},"inLanguage":"tr","potentialAction":[{"@type":"ReadAction","target":["https:\/\/www.cncmachiningshops.com\/metal-plating-process\/"]}]},{"@type":"ImageObject","inLanguage":"tr","@id":"https:\/\/www.cncmachiningshops.com\/metal-plating-process\/#primaryimage","url":"https:\/\/www.cncmachiningshops.com\/wp-content\/uploads\/2026\/06\/Metal-Plating-Process-Selection-800x600-1.jpg","contentUrl":"https:\/\/www.cncmachiningshops.com\/wp-content\/uploads\/2026\/06\/Metal-Plating-Process-Selection-800x600-1.jpg","width":800,"height":600,"caption":"Metal Plating Process Selection 800x600"},{"@type":"BreadcrumbList","@id":"https:\/\/www.cncmachiningshops.com\/metal-plating-process\/#breadcrumb","itemListElement":[{"@type":"ListItem","position":1,"name":"Home","item":"https:\/\/www.cncmachiningshops.com\/"},{"@type":"ListItem","position":2,"name":"Metal Plating Process Selection: How to Choose the Right Coating"}]},{"@type":"WebSite","@id":"https:\/\/www.cncmachiningshops.com\/#website","url":"https:\/\/www.cncmachiningshops.com\/","name":"CNC \u0130\u015fleme At\u00f6lyeleri","description":"10+ Y\u0131l CNC \u0130\u015fleme Hizmeti Tedarik\u00e7isi","publisher":{"@id":"https:\/\/www.cncmachiningshops.com\/#organization"},"alternateName":"CMS","potentialAction":[{"@type":"SearchAction","target":{"@type":"EntryPoint","urlTemplate":"https:\/\/www.cncmachiningshops.com\/?s={search_term_string}"},"query-input":{"@type":"PropertyValueSpecification","valueRequired":true,"valueName":"search_term_string"}}],"inLanguage":"tr"},{"@type":"Organization","@id":"https:\/\/www.cncmachiningshops.com\/#organization","name":"CNC \u0130\u015fleme At\u00f6lyeleri","alternateName":"CMS","url":"https:\/\/www.cncmachiningshops.com\/","logo":{"@type":"ImageObject","inLanguage":"tr","@id":"https:\/\/www.cncmachiningshops.com\/#\/schema\/logo\/image\/","url":"https:\/\/www.cncmachiningshops.com\/wp-content\/uploads\/2025\/11\/CMS_Logo_1000x1000.png","contentUrl":"https:\/\/www.cncmachiningshops.com\/wp-content\/uploads\/2025\/11\/CMS_Logo_1000x1000.png","width":800,"height":800,"caption":"CNC Machining Shops"},"image":{"@id":"https:\/\/www.cncmachiningshops.com\/#\/schema\/logo\/image\/"},"description":"Shenzhen CMS Technology Co., Ltd. Shenzhen, Guangdong, \u00c7in'de bulunmaktad\u0131r. 2012 y\u0131l\u0131nda 3.000 metrekare fabrika alan\u0131 ile kurulmu\u015ftur. CNC i\u015fleme ve hassas par\u00e7a \u00fcretimi konusunda uzmanla\u015fm\u0131\u015f bir \u015firkettir. ISO9001, IATF16949, ISO13485 sertifikalar\u0131na sahibiz ve g\u00fcvenilir orta\u011f\u0131n\u0131z\u0131z.","email":"info@cncmachiningshops.com","telephone":"+8617196430663","legalName":"Shenzhen CMS Technology Co., Ltd.","foundingDate":"2012-07-22","numberOfEmployees":{"@type":"QuantitativeValue","minValue":"11","maxValue":"50"}},{"@type":"Person","@id":"https:\/\/www.cncmachiningshops.com\/#\/schema\/person\/2593a2e2de68be71300e10f486236551","name":"cncmachiningshops","image":{"@type":"ImageObject","inLanguage":"tr","@id":"https:\/\/secure.gravatar.com\/avatar\/36a63d96ed08f8805561107422de4e83bbf8d1669dbc9655acab534bc3e1ed17?s=96&d=mm&r=g","url":"https:\/\/secure.gravatar.com\/avatar\/36a63d96ed08f8805561107422de4e83bbf8d1669dbc9655acab534bc3e1ed17?s=96&d=mm&r=g","contentUrl":"https:\/\/secure.gravatar.com\/avatar\/36a63d96ed08f8805561107422de4e83bbf8d1669dbc9655acab534bc3e1ed17?s=96&d=mm&r=g","caption":"cncmachiningshops"},"sameAs":["https:\/\/cncmachiningshops.com"]}]}},"_links":{"self":[{"href":"https:\/\/www.cncmachiningshops.com\/tr\/wp-json\/wp\/v2\/posts\/11783","targetHints":{"allow":["GET"]}}],"collection":[{"href":"https:\/\/www.cncmachiningshops.com\/tr\/wp-json\/wp\/v2\/posts"}],"about":[{"href":"https:\/\/www.cncmachiningshops.com\/tr\/wp-json\/wp\/v2\/types\/post"}],"author":[{"embeddable":true,"href":"https:\/\/www.cncmachiningshops.com\/tr\/wp-json\/wp\/v2\/users\/1"}],"replies":[{"embeddable":true,"href":"https:\/\/www.cncmachiningshops.com\/tr\/wp-json\/wp\/v2\/comments?post=11783"}],"version-history":[{"count":0,"href":"https:\/\/www.cncmachiningshops.com\/tr\/wp-json\/wp\/v2\/posts\/11783\/revisions"}],"wp:featuredmedia":[{"embeddable":true,"href":"https:\/\/www.cncmachiningshops.com\/tr\/wp-json\/wp\/v2\/media\/11853"}],"wp:attachment":[{"href":"https:\/\/www.cncmachiningshops.com\/tr\/wp-json\/wp\/v2\/media?parent=11783"}],"wp:term":[{"taxonomy":"category","embeddable":true,"href":"https:\/\/www.cncmachiningshops.com\/tr\/wp-json\/wp\/v2\/categories?post=11783"},{"taxonomy":"post_tag","embeddable":true,"href":"https:\/\/www.cncmachiningshops.com\/tr\/wp-json\/wp\/v2\/tags?post=11783"}],"curies":[{"name":"wp","href":"https:\/\/api.w.org\/{rel}","templated":true}]}}